Beater Add-Interface Materials
Click on material for description below:
| Equivalence Chart for Beater Add-Interface | |||
 |
|||
2331 - Standard/Nonasbestos Gasket Material
F339177E73M4
2331 is an environmentally compatible, low density gasket material formulated from recycled gasket materials. It has added styrene butadiene rubber binder, and is intended for general, light-duty applications with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 0.56 (35) (min.) | ASTM F 1315 |
| Compressibility, % (at 6.9MPa) | 15 - 35 | ASTM F 36 |
| Recovery, % | 35 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 6.90 (1000) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
|
Change in Thickness, % |
15 (max.) | |
| Change in Weight, % | 80 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 80 (max.) | |
| Fluid Resistance, Distilled Water | ASTM F 146 | |
| Change in Thickness, % | 55 (max.) | |
| Change in Weight, % | 80 (max.) | |
| Binder Type | Styrene Butadiene |
CN-705
F339199E99M9
CN-705 is a low-density, nitrile butadiene bound material that is suitable for use with oil, gasoline, and water. It is intended for use in applications with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 0.61 (38) (min.) | ASTM F 1315 |
| Compressibility, % (at 6.9MPa) | 25 - 40 | ASTM F 36 |
| Recovery, % | 25 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 5.52 (800) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 70 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 25 (max.) | |
| Change in Weight, % | 75 (max.) | |
| Fluid Resistance, Distilled Water | ASTM F 146 | |
| Change in Thickness, % | 25 (max.) | |
| Change in Weight, % | 50 (max.) | |
| Binder Type | Nitrile Butadiene |
CS-301
F339996E99M9
CS-301 has a controlled-swell styrene butadiene rubber binder. It is intended for use in applications with water, high analine point oil, and other applications not including aromatic fuels and certain solvents, and with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 0.61 (38) (min.) | ASTM F 1315 |
| Compressibility, % (at 6.9MPa) | 25 - 40 | ASTM F 36 |
| Recovery, % | 30 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 4.83 (700) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 30 (max.) | |
| Change in Weight, % | 105 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 35 (max.) | |
| Change in Weight, % | 95 (max.) | |
| Fluid Resistance, Distilled Water | ASTM F 146 | |
| Change in Thickness, % | 30 (max.) | |
| Change in Weight, % | 60 (max.) | |
| Binder Type | Styrene Butadiene |
N-2085G
F723940E43M6
N-2085G is a fully cured nitrile butadiene bound material that offers excellent resistance to water, coolant, oil, and fuel. This product is available in close tolerance gauges for hermetic compressor valve plate applications, and is intended for short duration maximum temperatures up to 190oC (375oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.36 (85) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 10 - 20 | ASTM F 36 |
| Recovery, % | 50 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 13.79 (2000) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 35 (max.) | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Change in Compressibility, % | 25 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Binder Type | Fully Cured Nitrile Butadiene |
N-8051
F339000M9, Z1
N-8051 is a light-duty material for low internal pressure and low flange pressure applications up to 13.8 MPa (2000 psi). It has a nitrile butadiene rubber binder for resistance to oil and is intended for applications with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Compressibility, % (at 2.76MPa) | 10 - 25 | ASTM F 36 |
| Recovery, % | 40 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 2.76 (400) (min.) | ASTM F 152 |
| Fluid Resistance, Oil #1 | ASTM F 146 | |
| Change in Volume, % | 35 (max.) | |
| Fluid Resistance, Fuel A | ASTM F 146 | |
| Change in Volume, % | 45 (max.) | |
| Binder Type | Nitrile Butadiene |
N-8090 - Syntheseal®/Nonasbestos Gasket Material
F724900E49M6
N-8090 has a latent cure nitrile butadiene rubber binder and reinforced cellulose fiber. It has excellent oil resistance, good sealing characteristics, and is intended for applications with short duration maximum temperatures up to 180oC (350oF). N-8090 has UL component recognition.
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.28 (80) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 25 | ASTM F 36 |
| Recovery, % | 35 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 13.79 (2000) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 45 (max.) | |
| Change in Thickness, % | 30 (max.) | |
| Change in Compressibility, % | 50 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 20 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Binder Type | Nitrile Butadiene |
N-8092 - Syntheseal®/Nonasbestos Gasket Material
F729900E59M9
N-8092 is used in automotive, small engine, and compressor applications. It has excellent crush resistance at high flange pressures, and excellent sealing properties with oil, fuel, and water. It is intended for applications with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.20 (75) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 30 | ASTM F 36 |
| Recovery, % | 35 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 11.03 (1600) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
|
Change in Tensile Strength, % |
30 (max.) | |
| Change in Thickness, % | 20 (max.) | |
| Change in Compressibility, % | 40 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 20 (max.) | |
| Change in Weight, % | 40 (max.) | |
| Binder Type | Nitrile Butadiene |
N-8094
N-8094 is a low density material that conforms well to irregular flange surfaces and has very good crush resistance at high flange pressures. It is intended for sealing oils, fuels, and water in applications with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 0.87 (54) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 28 - 42 | ASTM F 36 |
| Recovery, % | 20 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | ASTM F 152 | |
| Greater Than 1.2mm Gauge | 6.90 (1000) (min.) | |
| All Other Gauges | 8.62 (1250) (min.) | |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 30 (max.) | |
| Change in Thickness, % | 7 (max.) | |
| Change in Compressibility, % | 30 - 45 | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 7 (max.) | |
| Change in Weight, % | 25 - 50 | |
| Binder Type | Nitrile Butadiene |
NI-2085
F723940E43M6
NI-2085 has a nitrile butadiene rubber binder for resistance to water, coolant, oil and fuel. It has excellent strength and sealability characteristics, and is intended for applications with short duration maximum temperatures up to 190oC (375oF). NI-2085 has UL component recognition.
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.36 (85) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 10 - 20 | ASTM F 36 |
| Recovery, % | 50 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 13.79 (2000) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 35 (max.) | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Change in Compressibility, % | 25 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Binder Type | Nitrile Butadiene |
NI-2086
F723940E43M6
NI-2086 has a fully cured nitrile butadiene rubber binder for improved strength and fluid resistance. It is intended for applications with short duration maximum temperatures up to 190oC (375oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.36 (85) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 10 - 20 | ASTM F 36 |
| Recovery, % | 50 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 13.79 (2000) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 35 (max.) | |
| Change in Thickness, % | 10 (max.) | |
| Change in Compressibility, % | 25 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Binder Type | Fully Cured Nitrile Butadiene |
NI-2095A
F729150E92M9
NI-2095A is a cylinder head facing material designed to deliver the performance required by worldwide cylinder head applications. It is a non-asbestos material with inorganic fillers encapsulated by nitrile butadiene rubber, and is easy to combine on perforated metal core.
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.15 (72) (min) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 30 | ASTM F 36 |
| Recovery, % | 25 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 4.14 (600) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 30 (max.) | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 40 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 35 (max.) | |
| Binder Type | Nitrile Butadiene |
NI-2096
F729990E52M9
NI-2096 is a cylinder head facing material designed to deliver the performance required by worldwide cylinder head applications. It is a non-asbestos material with inorganic fillers encapsulated by nitrile butadiene rubber binder.
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.19 (74) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 35 (max.) | ASTM F 36 |
| Recovery, % | 20 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 4.48 (650) (min.) | ASTM F 152 |
| Weight Loss on Ignition, % (at 815oC) | 30 (max.) | ASTM F 495 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 45 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 40 (max.) | |
| Binder Type | Nitrile Butadiene |
NI-2097A
F729190E93M9
NI-2097A is a non-asbestos cylinder head facing material with inorganic fillers and fibers encapsulated by nitrile butadiene rubber binder. It is suitable for Original Equipment or Aftermarket use, combines easily on perforated metal core, and has good sealability and creep relaxation properties.
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.22 (76) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 35 (max.) | ASTM F 36 |
| Recovery, % | 30 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 3.10 (450) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 45 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 35 (max.) | |
| Fluid Resistance, Glycol/Water 50/50 | ASTM F 146 | |
| Change in Thickness, % | 30 (max.) | |
| Change in Weight, % | 80 (max.) | |
| Binder Type | Nitrile Butadiene |
NI-2098
F729990E52M2
NI-2098 is a heavy-duty cylinder head facing material that is used with both solid and perforated metal cores. It is a non-asbestos material with nitrile butadiene rubber binder, and is compatible with most polymers used in bead printing processes.
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.19 (74) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 30 | ASTM F 36 |
| Recovery, % | 20 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 1.72 (250) (min.) | ASTM F 152 |
| Weight Loss on Ignition, % (at 815oC) | 30 (max.) | ASTM F 495 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 20 (max.) | |
| Change in Weight, % | 55 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 40 (max.) | |
| Fluid Resistance, Glycol/Water 50/50 | ASTM F 146 | |
| Change in Thickness, % | 20 (max.) | |
| Change in Weight, % | 75 (max.) | |
| Binder Type | Nitrile Butadiene |
NI-2900
F729150E52M9
NI-2900 is a non-asbestos facing material designed to deliver the performance required by worldwide cylinder head and manifold applications. It has graphite and other inorganic fillers encapsulated by nitrile butadiene rubber binder, and is easy to combine on perforated metal core.
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.04 (65) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 27 - 37 | ASTM F 36 |
| Recovery, % | 18 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 3.79 (550) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 40 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 40 (max.) | |
| Fluid Resistance, Glycol/Water 50/50 | ASTM F 146 | |
| Change in Thickness, % | 25 (max.) | |
| Change in Weight, % | 60 (max.) | |
| Binder Type | Nitrile Butadiene |
NI-4002
F339997E92M9
NI-4002 is a non-asbestos facing material that, when combined on perforated metal core, is intended for elevated temperature applications such as exhaust systems. It has an inorganic filler system encapsulated by nitrile butadiene rubber binder, giving it low ignition loss and good torque retention properties.
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 0.88 (55) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 30 | ASTM F 36 |
| Recovery, % | 25 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 2.07 (300) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 70 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 55 (max.) | |
| Fluid Resistance, Distilled Water | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 80 (max.) | |
| Binder Type | Nitrile Butadiene |
NV-512
F333949E43M7
NV-512 is a cellulose fiber material with a fully cured nitrile butadiene rubber binder for increased strength and fluid resistance. It has very high tensile strength and crush resistance, and is used in applications such as air pumps, carburetors, gear boxes and transmissions. It is intended for applications with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 0.96 (60) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 10 - 20 | ASTM F 36 |
| Recovery, % | 60 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 20.69 (3000) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Fluid Resistance, Distilled Water | ASTM F 146 | |
| Change in Thickness, % | 35 (max.) | |
| Change in Weight, % | 50 (max.) | |
| Binder Type | Fully Cured Nitrile Butadiene |
NV-519
F332949E42M8
NV-519 is a cellulose fiber material with thermoset resin and nitrile butadiene rubber binder. It has excellent tensile strength, crush resistance, and erosion resistance against high volume fluid flow and impingement. It is used primarily in automatic transmission valve body, pump, and accumulator/channel plate applications as well as carburetors and air compressors. It is intended for use in applications with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 0.96 (60) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 5 - 15 | ASTM F 36 |
| Recovery, % | 60 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 27.59 (4000) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Fluid Resistance, Distilled Water | ASTM F 146 | |
| Change in Thickness, % | 70 (max.) | |
| Change in Weight, % | 70 (max.) | |
| Binder Type | Nitrile Butadiene |
NV-565
F339997E93M9
NV-565 is a low density cellulose fiber gasket material with a blend of rubber binders for good oil, fuel, and water resistance. It conforms well to irregular flange surfaces and is used primarily in carburetors, fuel systems, and water pumps. It is intended for applications with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 0.64 (40) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 30 | ASTM F 36 |
| Recovery, % | 40 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 12.07 (1750) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 10 (max.) | |
| Change in Weight, % | 65 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 65 (max.) | |
| Fluid Resistance, Distilled Water | ASTM F 146 | |
| Change in Thickness, % | 40 (max.) | |
| Change in Weight, % | 80 (max.) | |
| Binder Type | Nitrile Butadiene / Styrene Butadiene |
PF-4N - Pro-Formance®/MicroPore® Nonasbestos Gasket Material
F729000M9
PF-4N has a fully cured nitrile butadiene rubber binder for maximum fluid resistance. It has excellent sealability in a variety of environments and flange conditions. It is intended for applications with short duration maximum temperatures up to 290oC (550oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.44 (90) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 12 - 20 | ASTM F 36 |
| Recovery, % | 45 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 8.97 (1300) (min.) | ASTM F 152 |
| Binder Type | Fully Cured Nitrile Butadiene | |
| Remarks and Related Documents: | ||
| Specification values determined by the test methods required for ASTM F-104, Type 7 materials. | ||
RN-8011
F339099E09M9
RN-8011 is a low density cellulose fiber material with high rubber filler content and a nitrile butadiene rubber binder. It provides excellent sealing of oil and water at low flange pressures, and is used primarily for engine and transmission pan gaskets, water pumps, and environmental seals. It is intended for applications with short duration maximum temperatures up to 180oC (350oF). RN-8011 has UL component recognition.
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 0.61 (38) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 35 - 60 | ASTM F 36 |
| Recovery, % | 15 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 1.52 (220) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Weight, % | 120 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Weight, % | 120 (max.) | |
| Fluid Resistance, Distilled Water | ASTM F 146 | |
| Change in Weight, % | 45 (max.) | |
| Binder Type | Nitrile Butadiene |
S-207 Standard/Nonasbestos Gasket Material
F339999E99M9
S-207 is a cellulose fiber gasket material with controlled-swell styrene butadiene rubber binder. It is a suitable replacement for asbestos fiber gasket materials, saturated papers, and is used in many oil and coolant applications in the aftermarket. It is intended for use in applications with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 0.88 (55) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 10 - 30 | ASTM F 36 |
| Recovery, % | 30 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 9.66 (1400) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 35 (max.) | |
| Change in Weight, % | 70 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 50 (max.) | |
| Change in Weight, % | 65 (max.) | |
| Fluid Resistance, Distilled Water | ASTM F 146 | |
| Change in Thickness, % | 50 (max.) | |
| Change in Weight, % | 65 (max.) | |
| Binder Type | Styrene Butadiene |
S-8091
F724900E09M9
S-8091 is controlled-swell, Latent cure styrene butadiene bound material with reinforced cellulose fiber. It is intended for applications sealing oil, fuel, and low-pressure steam with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.20 (75) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 25 | ASTM F 36 |
| Recovery, % | 25 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 12.41 (1800) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 30 - 75 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Binder Type | Styrene Butadiene |
SV-360
F339197E93M5
SV-360 is a low density cellulose fiber material with styrene butadiene rubber binder. It is a general purpose material for anti-squeak, dust seals, heaters, oil seals, shim stock, and water pumps. It is intended for applications with short duration maximum temperatures up to 180oC (350oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 0.67 (42) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 30 | ASTM F 36 |
| Recovery, % | 40 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 10.34 (1500) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 70 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 70 (max.) | |
| Fluid Resistance, Distilled Water | ASTM F 146 | |
| Change in Thickness, % | 55 (max.) | |
| Change in Weight, % | 80 (max.) | |
| Binder Type | Styrene Butadiene |
TN-9000
F729900E33M9
TN-9000 has a fully cured nitrile butadiene binder with Aramid fiber. It has good tensile strength, low creep relaxation, and excellent fuel and oil resistance. It is intended for applications with high flange pressures and temperatures, with short duration maximum temperatures up to 400oC (750oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.44 (90) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 7 - 17 | ASTM F 36 |
| Recovery, % | 50 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 17.24 (2500) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 35 (max.) | |
| Change in Thickness, % | 10 (max.) | |
| Change in Compressibility, % | 30 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 20 (max.) | |
| Binder Type | Fully Cured Nitrile Butadiene |
TN-9001
F729900E49M6
TN-9001 is a heavy-duty latent cure material with nitrile binder. It has excellent oil resistance and is intended for applications with short duration maximum temperatures up to 400oC (750oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.28 (80) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 30 | ASTM F 36 |
| Recovery, % | 40 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 13.79 (2000) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 40 (max.) | |
| Change in Thickness, % | 20 (max.) | |
| Change in Compressibility, % | 35 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 30 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Binder Type | Nitrile Butadiene |
TN-9004
F729100E33M9
TN-9004 is a heavy-duty, high density material with fully cured nitrile butadiene rubber binder. It has excellent resistenace to fuel and oil, and has good tensile strength. It is intended for applications with high flange pressures with short duration maximum temperatures up to 350oC (650oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.52 (95) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 5 - 20 | ASTM F 36 |
| Recovery, % | 45 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 17.24 (2500) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 45 (max.) | |
| Change in Thickness, % | 15 (max.) | |
| Change in Compressibility, % | 25 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 20 (max.) | |
| Binder Type | Fully Cured Nitrile Butadiene |
TN-9005
F729900E59M5
TN-9005 is a heavy-duty material with a latent cure nitrile binder system. It conforms well to irregular flange surfaces, and is suitable for applications with short duration maximum temperatures up to 350oC (650oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.28 (80) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 30 | ASTM F 36 |
| Recovery, % | 25 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 10.34 (1500) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 50 (max.) | |
| Change in Thickness, % | 20 (max.) | |
| Change in Compressibility, % | 50 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 20 (max.) | |
| Change in Weight, % | 40 (max.) | |
| Binder Type | Nitrile Butadiene |
TN-9014
F729900E99M9
TN-9014 has a fully cured nitrile butadiene rubber binder and a blend of cellulose and Aramid Fibers. It has excellent fuel and oil resistance, and is intended for applications with short duration maximum temperatures up to 290oC (550oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.44 (90) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 7 - 20 | ASTM F 36 |
| Recovery, % | 45 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 17.24 (2500) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 45 (max.) | |
| Change in Thickness, % | 20 (max.) | |
| Change in Compressibility, % | 30 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 20 (max.) | |
| Change in Weight, % | 25 (max.) | |
| Binder Type | Fully Cured Nitrile Butadiene |
TN-9015
F729900E99M5
TN-9015 has a latent cure nitrile butadiene rubber binder and has a blend of Aramid and cellulose fibers. It conforms well to irregular flange surfaces and has excellent resistance to fuel and oil. It is intended for applications with short duration maximum temperatures up to 290oC (550oF). TN-9015 has UL component recognition.
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.28 (80) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 12 - 27 | ASTM F 36 |
| Recovery, % | 30 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 10.34 (1500) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 50 (max.) | |
| Change in Thickness, % | 25 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 25 (max.) | |
| Change in Weight, % | 35 (max.) | |
| Binder Type | Nitrile Butadiene |
TN-9040 Pro-Formance®/MicroPore® Nonasbestos Gasket Material
F729900E43M8
TN-9040 gasket material is a high density product with a fully cured nitrile butadiene rubber binder. It has excellent crush resistance, good creep relaxation properties and high tensile strength, and is recommended for application where high mechanical integrity is required. It is intended for applications with short duration maximum temperatures up to 290oC (550oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.49 (93) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 7 - 17 | ASTM F 36 |
| Recovery, % | 40 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 27.59 (4000) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Thickness, % | 20 (max.) | |
| Change in Compressibility, % | 30 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 30 (max.) | |
| Binder Type | Fully Cured Nitrile Butadiene |
TN-9045
F729900E93M5
TN-9045 is a heavy-duty material for use in elevated temperature applications. Its unique acrylic binder system adds additional temperature resistance over conventional rubber binders.
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.28 (80) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 10 - 25 | ASTM F 36 |
| Recovery, % | 45 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 10.34 (1500) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
| Change in Tensile Strength, % | 55 (max.) | |
| Change in Thickness, % | 25 (max.) | |
| Change in Compressibility, % | 30 (max.) | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
| Change in Thickness, % | 15 (max.) | |
| Change in Weight, % | 35 (max.) | |
| Binder Type | Acrylic |
TS-9003 - Thermo-Tork®/Nonasbestos Gasket material
F729900E09M4
TS-9003 is a controlled-swell gasket material with a latent cure styrene butadiene rubber binder. It is an alternative to high-swell asbestos and nonasbestos compressed sheet materials. Its latent cure binder and heat resistant fibers give it good oil sealing characteristics at low flange pressure, and it conforms well to irregular flange surfaces. It is intended for applications with short duration maximum temperatures up to 350oC (650oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.44 (90) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 30 | ASTM F 36 |
| Recovery, % | 20 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 6.90 (1000) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
|
Change in Thickness, % |
45 - 85 | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
|
Change in Thickness, % |
20 - 50 | |
| Binder Type | Styrene Butadiene |
TS-9006 - Thermo-Tork®/Nonasbestos Gasket Material
F729900E09M5
TS-9006 is a heavy-duty, high density gasket material with fully cured styrene butadiene rubber binder. It is recommended for use in oil, water, and steam applications with high flange pressures and short duration maximum temperatures up to 350oC (650oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.52 (95) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 5 - 20 | ASTM F 36 |
| Recovery, % | 40 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 10.34 (1500) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
|
Change in Thickness, % |
20 - 60 | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
|
Change in Thickness, % |
15 - 40 | |
| Binder Type | Fully Cured Styrene Butadiene |
TS-9003 Thermo-Tork®/Nonasbestos Gasket Material
F729900E09M4
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.44 (90) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 15 - 30 | ASTM F 36 |
| Recovery, % | 20 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 6.90 (1000) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
|
Change in Thickness, % |
45 - 85 | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
|
Change in Thickness, % |
20 - 50 | |
| Binder Type | Styrene Butadiene |
TS-9013 Thermo-Tork®/Nonasbestos Gasket Material
F729900E09M9
TS-9013 is a controlled-swell material with latent cure styrene butadiene rubber binder and a blend of Aramid and cellulose fibers. It conforms well to irregular flange surfaces and is intended for water and oil applications with short duration maximum temperatures up to 290oC (550oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.36 (85) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 12 - 25 | ASTM F 36 |
| Recovery, % | 25 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 8.28 (1200) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
|
Change in Thickness, % |
30 - 70 | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
|
Change in Thickness, % |
20 - 50 | |
| Binder Type | Styrene Butadiene |
TS-9016 Thermo-Tork®/Nonasbestos Gasket material
F729900E09M9
TS-9016 has a fully cured styrene butadiene rubber binder and a blend of Aramid and cellulose fibers. It is intended for oil and water applications with short duration maximum temperatures up to 290oC (550oF).
|
Property: |
Specification: |
Method: |
| Density, g/cc(lb/cu.ft) | 1.44 (90) (min.) | ASTM F 1315 |
| Compressibility, % (at 34.5MPa) | 10 - 25 | ASTM F 36 |
| Recovery, % | 40 (min.) | ASTM F 36 |
| Tensile Strength, AMD, MPa(psi) | 12.41 (1800) (min.) | ASTM F 152 |
| Fluid Resistance, IRM903 Oil | ASTM F 146 | |
|
Change in Thickness, % |
25 - 65 | |
| Fluid Resistance, Fuel B | ASTM F 146 | |
|
Change in Thickness, % |
10 - 40 | |
| Binder Type | Fully Cured Styrene Butadiene |
Flexoid Gasket Material (Detroiter Vegetable Paper)
F326128E21M6
Flexoid Gasket Material, also known as Detroiter Vegetable Paper, is a plasticized gelatin impregnated cellulose based material, a very economical gasket material with excellent oil and fuel resistance. Flexoid is recommended for applications where the maximum service temperature is less than 120º C. (250ºF).
|
Property: |
Specification: |
| Compressibility, % (at 6.89MPa) | 25 - 40 |
| Recovery, % | 40 (min.) |
| Tensile Strength, AMD, MPa(psi) | 2000 (13.79) |
| Fluid Resistance, Oil No. 3 | |
| Change in Thickness, % | 5 |
| Weight Increase, % | 15 |
| Fluid Resistance, Fuel B | |
| Change in Thickness, % | 5 |
| Weight Increase, % | 15 |
| Fluid Resistance, Distilled Water | |
| Change in Thickness, % | 30 |
| Weight Increase, % | 90 |